CUMILITE 60A SP
CUMILITE Mullite refractories are manufactured from high purity mullite grains. CUMILITE refractories are extremely stable in service, unlike conventional mullite refractories. They are specially meant for applications that demand good chemical and mechanical stability, strength at high temperatures and resistance to spalling, corrosion and flame impingement. They outperform other refractories in high temperature volume stability in applications such as high intensity burner, carbon black reactors and other processes operated at extremes of temperature and corrosive conditions. Mullite products based on Silimanite, Andalusite and sintered mullite are widely used in glass and steel industry applications for their excellent thermal shock properties, creep resistance and resistance to chemical attack.
| PRODUCT NAME | |
| PROPERTIES | UNIT |
| Maximum Hot Face Temperature | o C |
| Bulk Density | gm/cc |
| Apparent Porosity | % |
| Cold Crushing Strength | Kg/cm2 |
| Modulus of Rupture | Kg/cm2 |
| At Room Temperature | |
| At 1350o C | |
| Reheat Change | % |
| After heating at 1450°C for 6 hrs. | |
| Chemical Analysis | % |
| Al2O3 | |
| SiO2 | |
| Fe2O3 | |
| Recommended Laying Mortars | |
| CUMILITE 60A SPL | ||
| 60% Alumina , Andalusite based mullite product, higher strength | ||
| Limit Value | Typical Value | |
| 1550 | 1550 | |
| 2.50 min. | 2.55 | |
| 16.0 max. | 15.0 | |
| 650 min. | 650 | |
| 75 min. | 90 | |
| 40 min. | 50 | |
| +/- 0.25 max. | + 0.17 | |
| 60.0 min. | 60.5 | |
| 37.0 max. | 35.5 | |
| 1.0 max | 0.75 | |
| CUMIBOND LK 65 | ||
Note : The above typical values shown are based on average test result on standard samples. Properties are subjected to reasonable variation based on product shape etc. and hence should be considered for general guidence only.
CUMILITE Mullite refractories are manufactured from high purity mullite grains. CUMILITE refractories are extremely stable in service, unlike conventional mullite refractories. They are specially meant for applications that demand good chemical and mechanical stability, strength at high temperatures and resistance to spalling, corrosion and flame impingement. They outperform other refractories in high temperature volume stability in applications such as high intensity burner, carbon black reactors and other processes operated at extremes of temperature and corrosive conditions. Mullite products based on Silimanite, Andalusite and sintered mullite are widely used in glass and steel industry applications for their excellent thermal shock properties, creep resistance and resistance to chemical attack.
REFRAMAT furnishes quality industrial products across major industries, with prime focus on supply of Furnace Materials. we are serving the Steel Industry by host of products including supply of best quality Ferro Alloys. Our operations HO in New Delhi, covers several markets with our team putting constant endeavors to reach the clients for their Ferro Alloys needs in numerous industrial clusters including Ghaziabad, Kanpur, Sahibabad, Meerut (UP or Uttar Pradesh), Mandigobindgarh, Ludhiana, Jalandhar (Punjab), Baddhi, Kaleamb (HP or Himachal Pradesh), Ahmedabad, Rajkot, Surat, Baroda (Gujarat), Gwalior, Indore (MP or Madhya Pradesh), Raipur, Raigarh (Chattisgarh), Sonipat, Hissar, Faridabad (Haryana), J&K, Assam, Meghalya, Bhiwadi, Jaipur, Kota, Ajmer (Rajasthan), Kolkata, Durgapur, Asansol (West Bengal), Jharsuguda, Angul, Cuttack, Jajpur, Rourkela (Odisha), Vizag (Andhra Pradesh), Coimbatore, Chennai (Tamil Nadu), Mumbai, Pune, Nagpur (Maharashtra), Haridwar, Kashipur (Uttrakhand)…..